Średnica / Opakowanie
|
Średnice |
|
1 ea Tube |
4 ea Tubes/Box |
5 ea Tubes/Box |
5 lb Tube |
10 lb Tube |
25 lb Box |
|---|---|---|---|---|---|---|---|
| 15520R,15520S,15536R,15536S,15S0051 | |||||||
| .050" X 1/8" | 15620F1 | 1520FMPOP | 15620F15P | 15620F5 | |||
| .050" x 1/8" x 20" | 15620F | ||||||
| .050" x 1/8" x 36" | 15636F | ||||||
| .050" X 1/16" | 15320F1 | 15320F | |||||
| 1/8" | 15620R1 | 15636R | |||||
| 1/8" sq | 15620S1 | 15636S10 | 15620S | ||||
| 1/8" sq x 36" | 15636S | ||||||
| 1/16" | 15320R1 | 15320R | |||||
| 1/16" x 36" | 15336R | ||||||
| 3/32" | 15520R1 |
Wprowadzenie
Stay-Silv 15 has proven its value for many years as it has been considered the industry's standard 15% silver alloy. This filler metal is excellent for situations in where close fit-up does not exist and where thermal expansion and service vibration are involved.
Zalety
- A frequent choice for brazing copper, as copper is self-fluxing
- Wide melting range allows operators to fill loose connections and "cap", or build up around finished joint. When heated above its liquidus it will penetrate tight connections.
- Excellent for situations where close fit-up does not exist, and where thermal expansion and service vibration are involved.
- Popular brazing filler metal for HVAC and refrigeration connections.
- Can be used to braze brass with the use of appropriate brazing flux
- Suitable for brazing low nickel, (10% maximum), copper/nickel base metals
- Can be used for brazing copper-to-copper and copper-to-brass (using Stay-Silv" white brazing flux) applications.
- Corrosion resistance is generally similar to copper base metal, but phosphorus containing alloys should not be used if the braze is exposed to sulfur or sulfur compounds in service
- Not recommended for brazing steel or other ferrous metals due to sufficient lack of joint ductility
- Conforms to the EU Reach & RoHS directive